Stock Material: Agglomerated and sintered powder
Nominal composition:
MoB: base
Total boron: 8.0-8.5% wt.
Cobalt: 25-28% wt.
Chrome: 13.5-15% wt.
Coating Properties
apparent metallographic porosity: <1.5%
bond strength to carbon steel (@0.020" thick.): 10,000 PSI
hardness: 1000-1100 HV300
typical as-sprayed roughness Ra: 90-130 μin
maximal coating thickness: 0.030 in
maximal working temperature: 1,650 °F
|
Click on the image to enlarge it.
|
|
Click on the image to enlarge it.
|
Coating Characterization
The coating has good resistance to high temperature erosion
and sliding wear. Thermal shock resistance is fair. General
corrosion and high temperature corrosion resistance are very
good. Excellent anti-stick properties. The coating is inert to
molten metals (zinc, aluminum, etc.).
Typical Applications
Sliding wear and erosion at high temperatures, specifically
for work with molten metals (die casting parts, galvanizing
bath parts, sink roll, etc.).
|